Black Powder Coating Aluminum Alloy Extrusion , 6063 OEM Cabinet Material
Product Description
Delivery time: 15-20 days after receiving the deposite.
Payment term: 30% deposite and 70% balance after the delivery
Material: 6063 Alloy
Temper: T5
Brand name: Kaiyamei Aluminum
Finish: Mill Finished, Anodizing, Electrophoresis, Powder Coating ,Polish, Wood grain, Sand Blasting
Color: Clear Satin, Bronze, Black, Golden, Silver,
Thickness: 0.8mm - 1.5mm
MOQ: 500KG. Usually 12 tons for a 20 feet container; 24 tons for a 40 feet container.
Length: 5.8-5.98m, or as customer's request
Sample delivery: Two weeks (one week for mould +one week making sample)
Sample design: It is better we can get your drawing or sample, we mainly make according to your design, and we can keep confidential for your design.
Maximum extruder machine: 8000 tons; Minimum extruder machine: 500 ton
Delivery: About a month, it depends on quantity and size.
If the profiles are customized, we will make the sample first, after we get the confirmation from you, we will start production.
General Chemical Composition of Alloy
| Alloy | 6063(%) | 6061(%) | 6082(%) |
| Silicon Si | 0.20~0.60 | 0.40~0.80 | 0.7~1.2 |
| Iron Fe | 0.35 | 0.70 | 0.5 |
| Copper Cu | 0.10 | 0.15~0.40 | 0.1 |
| Manganese Mn | 0.10 | 0.15 | 0.4~0.8 |
| Manganese Mg | 0.45~0.90 | 0.18~1.2 | 0.6~0.8 |
| Chromium Cr | 0.10 | 0.04~0.35 | 0.25 |
| Zine Zn | 0.10 | 0.25 | 0.2 |
| Titanium Ti | 0.10 | 0.15 | 0.1 |
| Others(each) | 0.05 | 0.05 | 0.05 |
| Others | 0.15 | 0.15 | 0.15 |
| Aluminum | Remainder | Remainder | Remainder |
Mechanical Properties of Sections under Room Temperature
| Alloy | State | Tensile strength test | Hardness test |
| Tensile strength Rm M pa | Non-proportional Stretching Stress | Stretching rate | Pattern thickness | HV | HW |
| Rp0.2Mpa | (A50mm%) | mm | HV | HW |
| |
| 6063 | T4 | 130 | 75 | 14 | - |
| T5 | 160 | 110 | 8 | 0.8 | 58 | 8 |
| T6 | 205 | 180 | 8 | - |
| 6061 | T4 | 184 | 110 | 16 | - |
| T6 | 265 | 245 | 8 | - |
| 6082 (6351) | T4 | 205 | 110 | 12 | - |
| T6 | 290 | 250 | 6 | - |
Questions & Answer
| Q: What is aluminum extrusion, fabrication, and anodize? |
| A: Aluminum Extrusion refers to a process of creating shapes with an aluminum billet or log by forcing it to flow through a shaped opening in a die. Aluminum can be extruded into standard shapes or specific designs depending on a customer’s preference. |
| A: Aluminum Fabrication refers to building aluminum components by cutting, drilling, slotting, tapping,bending, CNC machining, mechanical assembly and welding. |
| A: Aluminum Anodize is an elector-chemical process of coating aluminum with a thin layer of oxide to increase corrosion resistance and harden the surface. |
| A: Aluminum also can be dyed with various anodizing colors, which in most widely used is Brone shades. |
Our company :
Foshan Kaiya Aluminum Co., Ltd is a comprehensive and professional enterprise integrating research, design production and sales of aluminium extrusion profiles for construction and industrial applications. There are currently 24 aluminum extrusion process lines at 500MT TO 2500MT, 5 process lines for anodizing, 3 process lines for powder coating, 2 process line for painting, 2process line of polishing and brushing. We still have 2 packing line. Our annual production capacity has reached 80,000 tons which is at the forefront of the aluminium industry in China.